Hello,
After many tests, it seems that ANY combination of hard aggregates in my castings produces holes here and there which I try to prevent as much as possible.
what is the best mix ratio from cement/sand ( no hard aggregates) for thin castings such as bowls and planters?
I know that...
Thanks for your in depth answer.
I dont know what GGBS i tried to look online but not sure where i can find it in israel and what they call it here
the mix you suggest has no aggragres, is this ok?
Thanks,
Dor
Thanks a lot for this information my friend.
I tried to used fibers but it seems to really made the mix not workable. i will buy a superplastizer and try again with it, thanks :)
The casting of 10-20 mm is usually the thickness of the end concrete bowl that is coming out of the plastic mold...
Thanks for your replay!
I am casting concrete candle holders, the can go to about 1 cm so i am looking for a grade or a custom mix that will prevent cracks as much as possible in the future.
I am using sea sand but also have "regular" construction sand( dry), so i can use it if needed...
High-strength concrete grade is more ideal than a low-strength grade when casting into molds such as plastic bowls and silicone molds? I am using 0.3mm gravel along with sea sand as aggregates.
Crack -safe is important! :)
Many thanks!