Sir Why debonding of cement paste and dado occurs

Sir, Why there is different dia for different grades as well grade of steel. What will happen if we use the mandrel of different than mentioned. One more question is can bend steel used again by rebending them

Sir, Can you please explain the treatment of honeycombing in detail

[ Dnyan sir please correct me if I'm wrong

For slump cone 25 no of blows per layer and cone should be filled in 4 layers. For preparation of specimen for compression test mould should be filled in 3 layer and no of blows should not be less than 35 per layer If you read carefully (IS 516 clause no 2.10.1) it is clearly said that no of...

As per IS 516 for 150mm mold size it is given as blows should not be less than 35 per layer & for 100 mm mold size it should not be less than 25

sir, First of all thanks for such nice information & arranging them in very good manner My question is many times in case of flow concrete we didnt get the required flow though we had used same proportion as mentioned in CMD. So is it good to add some extra admixture, what is the best way to...

Which cement should be preferred for plaster to avoid cracks. Does fineness affect the strength of cement & how

Great sir, I really appreciate it. Thanks alot

Yes sir understood Thanks

Why the proportions of M 30 and above grade of concrete are not given in is 456

Nice work sir Sir can you please provide me how the rate analysis of brickbat coba is done